Polycaprolactone (PCL)/calcium carbonate composite was made by blending PCL and master Batch (MB). Wheatherability, biodegrability, thermal properties, mechanical properties and water absorption of PCL/calcium carbonate composite were investigated. After 45days, the biodegrability increased with increasing the content of MB. Tensile strength and elongation decreased but tensile modulus maintained with increasing the time of outdoor exposure in spring. Tensile strength, elongation and tesile modulus decreased with increasing the time of outdoor exposure in summer. Compared with the results of whetherability experiment in spring, it was found that the decreasing rate of tensite strength and elongation were similar in PM10, PM30 but higher in PM50, PM70. The melting temperature of PCL/MB composite was about 57℃. The water absorption of PCL/MB was higher than PCL. But the change of water absorption by the content of MB could be ignored because the total water absorption of PCL/MB composite was lower than 1%.

Polycaprolactone (PCL)과 탄산칼슘이 주성분인 master batch (MB)를 블랜드하여 PCL/MB 복합체를 제조하였다. PCL/MB = 90/10, 70/30, 50/50, 30/70에 대해서 내후성, 생분해도, 열적특성, 기계적 물성, 흡습성 등을 측정하였다. 45일간의 생분해 실험 후 PCL/MB 복합체에서 MB의 함량이 증가함에 따라 생분해도가 증가하였다. 그리고, 봄철 옥외 자연광 노출 실험에서 자연광 노출 시간이 증가함에 따라 파단점에서의 인장강도와 신장율은 감소하였고 탄성율은 비교적 일정하게 유지되었다. 여름철 옥외 자연광 노출 실험에서는 MB의 함량이 증가함에 따라 인장강도, 신장율, 탄성율이 감소하였고 봄철 실험결과와 비교해 보았을 때 PM10, PM30에서는 파단점에서의 인장강도와 신장율이 거의 비슷하였으나 PM50, PM70의 경우에는 크다는 것을 알 수 있었다. PCL/MB 복합체의 용융온도는 전조성에서 대략 57℃로 MB의 영향을 거의 받지 않았다. PCL/MB 복합체의 수분 흡수율이 PCL 보다 약간 큰 값을 나타내었지만 전체 흡수율이 1%도 채 되지 않았기 때문에 MB에 의한 흡수율의 변화가 거의 없었다.