Graphite-Nylon6 composites were prepared by anionic polymerization of ε-caprolactam in the presence of artificial graphite powder. Volume resistivities and mechanical properties of composites containing graphite from 0.5 phr to 8 phr were measured, and the dispersities of graphite were observed by optical microscopy. Electric conductivities of the composites were dependent on the particle size of graphites as well as of the graphite content, and the composites containing graphite over 2 phr showed volume resistivities in the range of 107∼ 106Ωcm. In particular, electric conductivities of the composites were significantly affected by the dispersity of graphite on the matrix. Little decreases in mechanical properties were observed for the composites with graphite content of 2 phr, which are applicable for antistatic purpose.

인조 그래파이트 입자의 존재하에서 ε-caprolactam을 음이온 중합시키므로써 대전방지용 나일론6 복합체를 제조하였다. 그래파이트를 0.5~8 phr 함량으로 첨가하여 제조한 sample의 체적고유저항 및 기계적 물성을 측정하였고, 광학현경을 통하여 그래파이트으 분상상태를 관찰하였다. 복합체의 전기 전도도는 첨기된 그래파이트 함량과 종류에 영향을 받는 것으로 확인되었고, 그래파이트 함량 2phr 이상에서 대전방지용으로 사용가능한 107~106Ωcm의 체적고유저항치를 나타내었다. 복합체의 전기 전도도는 그래파이트 입자의 분산상태에 크게 영향을 받는 것으로 확인되었으며, 그래파이트 입자가 domain을 형성할 때 복합체에 전기 전도성이 부여되었다. 대전방지용으로 사용가능한 그래파이트 함량 2phr에서 기계적 물성의 저하는 거의 없었다.