The latex IPN was prepared with monomer mixture system[(MMA+BMA)]by two stage emulsion polymerization. The influence of crosslinking agent content on damping properties were analyzed. Especially, reactive latex IPN was prepared using AA and GMA on the stage Ⅰand Ⅱ, respectively. Also, the effect of the functional crosslinking on damping properties of reactive latex. IPN was investigated, As increasing crosslinking agent contents, the 2nd stage material (BA) cannot be different into the 1st stage particle (MMA+BMA). That makes to separated phase, finally the 2nd stage material (BA) forms continuous phase bulk specimen preparation by the damping behaviors of the LIPN. In the damping behaviors of the reactive latex IPN, it was shown that the compatibility of two phase seemed to be dependant on the content of functional monomer. The phase separation behavior of reactive latex IPNs was inhibited by the formation of the network structure and the functional crosslinking of carboxy and epoxy group.

단량체 혼합물인 [(MMA+BMA)/BA]를 2단계 에멀젼 중합법에 의하여 라텍스 IPN을 제조하였으며 가교제의 함량에 따른 damping 성질을 분석하였다. 특히 제1단계에 AA, 2단계에 GMA를 각각 첨가하여 기능성 라텍스 IPN을 제조하였으며, 기능성 단량체의 도입에 따른 functional crosslinking의 효과가 damping 성질에 미치는 영향과도 비교 분석하였다. LIPN의 damping 거동은 가교제의 함유량이 증가할수록 제2단계 물질(BA)이 제1단계 입자 (MMA+BMA)내로 확산되기 어려워분리된 상을 형성하고 시편의 제조동안에 제2단계 물질(BA)이 연속상을 형성하게 됨을 알 수 있다. 기능성 라텍스 IPN의 damping 거동은 두 상의 상용성이 기능성기 함량에 의존하고 있음을 보여주었다. 기능성 라텍스 IPN은 가교제에 의한 network 구조의 형성과 carboxy기와 epoxy기에 의한 functional crosslinking의 효과로 더욱 상 분리 현상을 억제하고 있다