We have studied the adsorption, surface properties and anitbacterial effects of Ag-treated PAN based activated carbon fiber. From the adsorption studies on the series of Ag-treated activated carbon fiber, typical Type I isotherms were obtained. And also, their adsorbed volume drasically decrease with the increase in the mole ratio of Ag on the treated activated carbon fiber. The specific surface areas of the metal treated activated carbon fiber obtained from BET equation were in the range of 113.183~1574.13 ㎡/g. From the αs-method, 0.059~1.09㎤/g of the micropore volumes were obtained. And from the SEM morphology results, it was observed that the surface of activated carbon fiber are partially blocked and coated by metal after the treatment. Finally, from the antibacterial effects of Ag-treated activated carbon fiber against. E. coli, the areas of antibacterial effect become larger with the increase in mole ratio of Ag treated.

본 연구에서는 Ag를 처리한 PAN계 활성탄소섬유에 대하여 흡착 및 표면특성을 통하여 물리화학적 특성을 제시하였다. Ag-ACF에 대한 흡착특성연구로부터 대표적인 Type I의 등온곡선을 얻을 수 있었고, 이들 등온곡선으로부터 Ag를 처리한 몰비를 증가시킴에 따라 흡착량이 급격히 감소함을 알 수 있었다. BET식으로부터 금속이 처리된 활성탄소섬유의 비표면적을 구한 결과 113.183~1574.13㎡/g의 범위에 분포하였다. 또한 αs-법을 사용하여 구한 미세 동공부피는 0.059~1.09㎤/g의 범위에 분포함을 알 수 있었다. 이와 관련하여 SEM 분석을 통하여 표면성상에 대하여 연구한 결과, 처리된 금속은 섬유표면 주위를 부분적으로 또는 전범위에 걸쳐서 피복되어 있음이 관찰되었다. 최종적으로 대장균(E, coli)에 대한 Ag-ACF의 향균특성에 대한 결과로부터 Ag의 양이 증가함에 따라 향균효과가 크게 증가함을 알 수 있었다.