Research Papers : Effect of Electrolytes on Synthesis of Monodispersed Al2O3 Fine Particles in Mixed Solvents
Abstract
To obtain unagglomerated, narrow size distributed, and monodispersed Al2O3fine particles from Al(sec-OC4H9)3, emulsion method was used. Acetonitrile as a hydrophilic solvent and n-octanol as a hydrophobic solvent were used in order to control the hydrolysis rate of Al(sec-OC4H9)3. Electroytes were added in mixed solvent to prevent the fine particles from aggregating and its effect was investigated. It was found that optimal synthetic conditions of monodispersed alumina fine particles were 0.05M Al-alkoxide, 0.1M H2O, 50 vol% n-octanol, 40 vol% acetonitrile, 10 vol% ethanol, and 10-2M HCI under 10℃ reaction temperature.
연구논문 : 혼합용매내에서 단분산 Al2O3 미립자의 합성에 대한 전해질 첨가 효과
초록
에멀젼법을 이용하여 가수분해 속도가 빠른 Al (sec-OC4H9)3로부터 응집이 없고 입도 분포가 좁은 단분산 알루미나 미립자를 얻었으며 가수분해 속도를 조절하기 위하여 소수성 용매인 n-octanol과 친수성 용매인 acetonitrile의 혼합 용매를 이용하였다. 또한 분산상의 안정성을 유지하여 생성된 미립자의 응집을 방지하기 위하여 혼합용매에 전해질을 첨가한 후 이들의 효과를 살펴보았다. 실험결과, 단분산 알루미나 미립자를 얻기 위한 최적조건은 온도 10℃에서, Al (sec-OC4H9)3, 0.05M, H2O 0.1M, 50 vol% n-octanol, 40 vol% acetonitrile, 10 vol% ethanol이었으며, 이때 전해질 HCI의 농도는 10-2M 이었다.