Maxwell displacement current (MDC) measuring technique has been applied on the study of monolayers of polyamic acid containing azobenzene. The displacement current was generated from monolayers on the water surface by monolayer compression and expansion. Displacement current was generated when the area per molecule was about 140Å2and 100 Å2. Maxwell displacement currents were investigated in connection with monolayer compression cycles. It was found that the maximum of MDC appeared at the molecular area just before the initial rise of surface pressure in compression cycles. The absorption spectra of polyamic acid containing p-methoxyazobenzene in a mixture of N, N-dimethylacetamide (DAMc) and benzene (1:1 by volume) solution was induced photoisomerization by UV and visible light irradiation. Ultra thin film of polyamic acid containing p-methoxyazobenzene was prepared on the hydrophilic quartz plate by Langmuir-Blodgett (LB) method. The precursor LB film was heated in a vacuum dry oven at 120℃ in order to convert it into the LB film of polyimide. The absorption spectra of LB films were also induced photoisomerization by UV and visible light irradiation.

아조벤젠을 함유한 polyamic acid를 수면상에서 전개시킨 Langmuir 막의 Mawell 변위전류, polyamic acid의 용액상태에서의 광이성질화 현상, 온도 변화에 다른 흡광도 변화, Langmuir-Blodgett (LB) 막을 누적시켜 열처리 및 광조사에 따른 물성 변화를 측정하였다. 먼저 변위전류를 검토한 결과 변위전류의 최대치는 1차 압축과 2차 압축시 모두 표면압이 상승되기 직전의 분자 점유 면적에서 나타남을 알수 잇었으며, 1차 및 2차 압축, 확장시 1차에 비해 2차의 경우 변위전류, 전하량 및 표면압의 분자당 점유면적이 감소하는 형상이 나타났다. 또한 polyamic acid 용액의 온도 변화에 따른 흡광도를 측정한 결과 용액의 온도가 상승함에 따라 흡광도가 증가함을 볼 수 있었으며, 이 용액에 대하여 광조사를 시도한 결과 광이성질화 현상에 대하여 가역적인 변화가 나타남을 볼 수 있었다. 그리고 polyamic acid의 LB 단분자막의 열처리 영향을 조사한 결과 열처리를 하기 전 보다 열처리한 후 흡광도가 상승하는 경향을 나타내었으며 polyimide LB 단분자막의 열처리하여 광조사를 한 결과 광이성질화 현상을 관찰할 수 있었다.