Poly(ethylene glycol)-containing alkyd resins were prepared for the dispersing agent and binder by reacting the carboxy-terminated poly(ethylene glycol) with 1,1,1-trimethylolpropane monostearate obtained from 1,1,1-trimethylolpropane and stearic acid. Dispersing properties of titanium dioxide and talc were compared by measuring transmittance of the dispersing solutions, and rate of the sedimentation in 1,1,1-trichlorethane. These alkyd resins, which contained both hydrophilic and lipophilic parts, showed a good dispersion of the polar inorganic particles in the non-polar solvent. The dispersing effect of the PEG-containing alkyd resins showed its maximum when the molecular weights of hydrophilic and lipophilic parts were almost the same. This happened when the alkyd resin was prepared from PEG 1000, which turned out to agree well with HLB value 10.25.

Polyethylene glycol (PEG) 단위를 포함하는 알키드 수지를 무기 안료인 이산화 티탄(TiO2) 및 활석 (talc)의 바인더 겸 분산제로서의 응용성을 알아보기 위하여 여러 가지 분자량의 카르복시기를 말단에 가지는 PEG와 stearic acid와 1,1,1-trimethylolpropane으로부터 합성된 디올과의 축합 중합에 의하여 합성하였다. 이들을 1,1,1-trichloroethane (TCE) 용매 중에 용해하고 이산화 티탄과 활석을 분산하여 투광도 및 시간에 따른 침강 속도를 측정하고 분산성을 비교하였다. PEG 단위를 포함하는 알키드 수지는 수지 중에서 친수성 부분과 소수성부분을 동시에 가지고 있어서 극성을 가지는 무기 미립자들이 비극성 용매 중에서 좋은 분산성을 보여주었다. PEG 1000을 사용하여 합성한 알키드 수지의 HLB 값은 10.25이었으며 이는 친수성 부분과 소수성 부분의 비가 약 1이 되는 것으로 TCE 용매 중에서 무기 미립자들의 분산성이 가장 우수하였다.