Asymmetric porous polyetherimide(PEI) membranes were prepared from PEI/N-methy2-pyrrolidone (=25/75 wt%) solution by the phase inversion method and their skin layer was modified with 0.25 M NaOH solution. The permeation of the gases (CO2, N2) through the modified PEI membranes in dry or wet conditions were studied under various perssures and temperatures compared to the results of unmodified PEI membranes. In a dry condition, the gas permeance through the modified PEI membranes was reduced greatly, but the selectivity increased slightly compared to unmodified one. However in a wet condition, the permeance also decreased but the selectivity increased greatly due to the blocking effect of water vapor. The modification of the PEI membrane with NaOH solution reduced the pore size of the membrane and enhanced the hydrophility of the membrane surface

상전이 공정에 의해 개조된 비대칭 다공성 PEI막을 0.25M NaOH 수용액에 일정 시간동안 침지시키는 방법으로 막의 표면을 개질한 다음 마른(dry)상태 및 젖은(wet)상태에서 운전압력과 온도 변화에 따른 기체투과 거동을 살펴보았으며, 이를 표면개질 전의 기체투과 거동과 비교하였다. 그 결과, 표면개질에 의하여 PEI막의 친수성은 크게 향상되었으며 기공의 크기는 약간 감소하는 경향을 보였다. 특히 표면개질한 막의 경우 젖은 상태에서 수분에 의한 막의 기공 막힘 현상이 뚜렷하게 나타나 표면개질 않은 막에 비해 기체의 투과도는 약간 감소하였으나 N2에 대한 CO2의 선택도는 크게 향상되는 결과를 보였다.