Different amounts of zinc stearate were incorporated as a plasticizer into poly(styrene-co-sodium methacrylate) ionomers prepared by bulk-suspension plymerization and neutralization with sodium hydroxide and effects of the zinc stearate on the thermal and rheological properties were investigated. It was obseved that the crystallization of zinc stearate in the ionomers were partially suppressed depending on the content of ionic moieties. It is postulated that the ionic moieties dissolved zinc stearate and suppressed crystallization of the zinc stearates. We speculated that 0.4∼0.6 mole of zinc stearate was dissolved by one mole of the ionic moiety. Poly(styrene-co-sodium methacrylate) containing only the dissolved zinc stearates showed typical rheological properties of homogeneous systems in Cox-Mertz plots. However, poly(styrene-co-sodium methacrylate) containing crystallizable zinc stearates as well as dissolved ones showed typical rheological properties of heterogeneous systems.

괴상 중합과 현탁 중합 및 수산화나트륨을 이용한 중화를 통하여 제조된 poly(styrene-co-sodium methacrylate) 이오노머의 가소제로 스테아린산 아연을 첨가하여 열적 성질과 유변학적 성질에 미치는 영향을 조사하였다. 이오노머 중 스테아린산 아연은 이온기 함량에 따라 부분적으로 결정화가 억제됨이 관찰되었다. 이오노머 중 이온기들은 스테아린산 아연을 용해시키고 결정화를 억제하는 것으로 판단되었으며, 이온기 1몰이 0.4∼0.6몰의 스테아린산 아연을 용해시키는 것으로 추정할 수 있었다. 용해된 형태의 스테아린산 아연만을 포함한 이오노머는 Cox-Merz 플롯에서 전형적인 균일계의 유변학적 거동을 보였다. 그러나 용해된 스테아린산 아연뿐 아니라 결정성 스테아린산 아연을 포함한 이오노머들은 Cox-Merz 플롯에서 불균일계의유변학적 거동을 보였다.