By using a liquid-mix precursor, we prepared the hollow glass spheres(HGS) as an additive of polymer compound which are used in the field of modifier, promoter, filler, and reinforcement. Liquid-mix precursor is a mixture of 40% sodium silicate aqueous solution, boric acid as a insolubilizing agent, and urea as a blowing agent. To obtain the precursor particles which are fed into a gas flame furnae, the above liquid-mix precursor was dried in oven and crushed with ball mill. We assumed the size of precursor particles (53∼63㎛, 63∼180㎛), temperature of furnace(800∼1200℃), and amount of urea(0∼30 g) as the parameters affecting on the properties of HGS. As a result mean particle size of HGS increases with increasing the temperature of furnace and the amount of urea and with decreasing the size of precursor particles. Also, we found that incresing the amount of urea is related to a decrease of the crush strength of HGS.

고분자 화합물의 첨가제로서 개질제, 물성 향상제, 충진제, 강화제 등의 용도로 사용되고 있는 유리 중공구체를 혼합액상 전구체를 사용하여 제조하였다. 혼합액상 전구체는 40% 규산나트륨(Na2O : SiO2= 1:2) 수용액에 불용제인 붕산과 팽창제인 요소를 혼합한 용액이며, 이 용액을 오븐에 건조시킨 후, 볼밀로 분쇄시켜 기체 화염로에 투입될 원료 입자를 제조하였다. 유리 중공구체의 물성에 영향을 미치는 인자로서는 로에 투입될 원료 입자의 크기(53∼63㎛, 63∼180㎛)와 로 내부의 온도(800∼1200 ℃), 그리고 요소의 변화량(0∼30 g)을 택하여 실험하였으며, 실험 결과 유리 중공구체의 평균 입경은 원료 입자의 크기가 작을수록, 로 내부의 온도가 클수록, 그리고 요소의 조성이 증가할수록 증가하는 결과를 보여 주었다. 또한, 유리 중공구체의 파쇄 강도는 요소의 양이 증가할수록 감소하는 경향을 나타내었다.