sothemal reduction at 50 ℃ using Pt/MoO3or Pt/MoO3/SiO2made by dry impregnation or physical mixture of Pt°and MoO3demonstrated that the H2uptake vis H2spillover from Pt into MoO3was enhanced as calcination temperature was increased. Surface area of exposed Pt crystallites measured by CO chemisorption was decreased with higher calcination temperature. In addition, TEM showed that MoOxoverlayers were formed on Pt crystallites after calcination at 400℃. Consequentially, it was found that this increased active contact sites between Pt and MoO3due to surface morphological change was one of the dominant factors for this increased H2uptake via H2spillover from Pt crystallites into MoO3.

함침법에 의하여 제조된 Pt/MoO3와 Pt/MoO3/SiO2및 Pt°와 MoO3를 기계적으로 혼합한 촉매를 사용한 50 ℃ 등온 환원 실험에서 소성 온도가 증가할수록, H2spillover에 의하여 Pt로부터 MoO3로 이동하여 저장되는 H2가 증가하는 것을 측정하였다. 연속적으로 실행한 CO chemisorption에 의하여 H2spillover에 참가하는 H2에 노출된 Pt 표면적이 감소하는 것을 알 수 있었다. 또한, TEM 결과로부터 400℃에서 소성 후 Pt결정 표면에 MoOxoverlayer가 형성되는 것을 관찰하였다. 그러므로, 표면 형상 변화에 따른 Pt과 MoO3간의 활성접촉점 증가가 H2spillover에 의한 MoO3로의 H2이동을 증가시키는 원인 중의 하나인 것으로 판명된다