RESEARCH PAPERS : Stabilization of LiMnO4 Electrode for Lithium Secondary Battery (2) - Stability of Substituted LMnO4 in Aqueous System -
Abstract
Stability of a cathode material was determined by Tafel plot in 1 M LiOH solution. The stabilized LiMxMn2-xO4(x=0.05∼0.1) electrode resulted in overpotential of 0.13∼0.15 mV at 100 mA. This overpotential was 0.05 mV lower than that of the spinel structured LiMn2O4electrode. Conductivity test at various potentials showed that the conductivity of LiMxMn2-xO4was higher than that of the spinel structured LiMn2O4and the bulk resistance of LiMxMn2-xO4due to the dissolution of Mn2+was lowered.
연구논문 : 리튬이차전지용 정극활물질 LiMn2O4 의 안정화 (2) - 수용액계에서 치환형 LiMn2O4 의 안정성 -
초록