Asymmetric polyetherimide membrane were prepared by phase inversion method, and the effects of NaOH concentration and reaction time on the morphology change of the polyetherimide membranes were studied . The morphology of skin layers varied from dense structure to sphere structure with increasing concentration of modification solution. The thickness of dense layer increased with increasing reaction time. However, when either the concentration of modifying solution was very high or the reaction time was very long, the dense layers of the asymmetric membrane were disappeared. From these results, it was found that the surface morphology of the asymmetric polyetherimide membranes depended strongly on the modification conditions such as concentration of modification solution and reaction time. These results might be explained by the hydrolysis reaction of polyetherimide into polyamic acid by the NaOH solution.

상분리 방법으로 비대칭 폴리에테르이미드막을 제조하였고, 수산화나트륨 수용액으로 막의 표면층을 개질 했을 때의 몰폴로지 변화를 반응기간과 반응용액 농도에 대하여 살려보았다. 표면층 몰롤로지는 개질 용액의 농도가 증가함에 따라 치밀한 구조에서 둥근 입자상의 형태로 변화되었고, 개질 시간이 증가될수록 치밀 영역이 증가되었다. 그러나 반응 농도가 아주 높거나 장시간 개질을 하면 비대칭폴리에테르이미드막의 표면에서 치밀 구조층이 없어지는 결과를 나타냈다. 결과적으로, 표면의 몰폴로지는 개질 용액의 농도와 시간에 따라 크게 좌우됨을 알 수 있었다. 이러한 결과는 폴리에테르이미드가 수산화나트륨에 의해서 폴리아믹산으로 가수분해되면서 나타나는 현상으로 추측되었다.