The films annealed after physical deposition of titanium and chemical deposition of amorphous silicon by plasma were formed Si-rich titanium silicide with a good quality of crystallinity and had the various lattice structures due to orientation of lattices for epitaxy growth during annealing process. Band gap of the titanium silicide had 1.14∼1.165 eV and the films annealed after chemical deposition of a-Si:H by plasma were influenced by a-Si and the dangling bond offered by desorption of hydrogen. Urbach tail (E0) of the films annealed after physical deposition of Ti was nearly constant within a range of 0.045∼0.05 eV, and the number of defect in films annealed after chemical deposition of a-Si:H by plasma was about 2∼3 times more than that in annealed Ti/Si films.

티타늄을 물리증착시킨 후 열처리한 막과 플라즈마에 의해 무정형 실리콘을 증착시킨 후 열처리한 막은 양질의 결정성을 갖는 Si가 풍부한 티타늄 실리사이드가 형성되고, 열처리 과정에서 에피택시 성장을 위한 격자들의 회전에 의해 다양한 형태의 격자구조를 갖는다. 티타늄 실리사이드 막의 band gap은 플라즈마에 의해 a-Si:H 막을 증착시킨 후 열처리한 막이 수소의 탈착에 의해 제공된 dangling bond, a-Si 등의 영향을 받아 1.14∼1.165 eV의 값을 가진다. 물리증착하여 열처리한 막의 Urbach tail인 E0는 0.045∼0.05 eV 범위로 거의 일정하고, 플라즈마에 의해 a-Si:H 막을 증착시킨 후 열처리한 막의 결함수는 Ti/Si를 열처리했을 때 얻어진 결함수보다 약 2∼3배 정도 많은 것으로 나타났다.