We have investigated various kind of graphite and MCMB6-28 to develop carbon negative electrode for lithium ion secondary battery. The interalyer length of them was 3.358∼3.363Å and the BET specific surface area was 2.95∼26.15㎡/g. From this study, When the interlayer of them was large and the BET specific surface area was high, the electrochemical characteristics of them was very excellent. Adding 0, 3, 5, wt% of KJ-Black as conducting agent to various graphitic carbon active materials, interface resistance of electrode and electrolyte was less, but rechargeability was better at 3 wt%. At constant current charge and discharge test, discharge capacity was small according to large current

본 연구는 리튬이온 이차전지용 탄소전극을 개발하기 위하여 다양한 종류의 흑연과 MCMB6-28을 대상으로 이루어졌다. 이들의 층간거리는 3.358∼3.368Å, BET 비 표면적은 2.95∼26.15㎡/g이었다. 이들의 전기화학적 특성은 층간거리가 크고 적절한 크기의 BET 비 표면적을 가질 때 리튬의 삽입과 탈삽입 거동이 우수하였다. 다양한 결정성계 탄소전극 활물질에 도전재로 KJ-Black을 0, 3, 5wt% 첨가하였을 때 도전제의 함량이 많을수록 전극과전해질의 계면저항은 작아지나 3wt%를 첨가하였을 때 우수한 가역성을 보였다. 정전류 충·방전 시 인가되는 전류밀도를 증가시킴에 따라 탄소부극의 방전용량은 작아졌다