Hydrated aluminum sulfate, an inorganic polymer, was synthesized from kaolin in H2SO4solution using microwave energy. The maximum rates of alumina extracted from calcined kaolin were 72.8% in a conventional process (80℃, 1M, and 180min) and 99.9% in a microwave process (90℃, 1M, and 60 min). Compared with the conventional one, the hydrated aluminum sulfate synthesized under the microwave process had layer structure consisting of plate-shaped large grains. After synthesis and then calcination at 1100℃, both products on conventional and microwave processes were γ-Al2O3with agglomerated powders of spherical shape. The specific area of the products in conventional and microwave processes were 113.5 and 106.6m2/g, and their average grain sizes were 46.5 an 26.3 ㎛, respectively.

마이크로파 열원을 이용하여 황산 용액에서 카올린을 가열 반응시켜 무기고분자인 수화 황산 알루미늄을 합성하였다. 하소된 카올린으로부터 알루미나의 최대 추출율은 재래식 열공정 (80 ℃, 1 M 및 240분)에서 72.8%이었고, 마이크로파 공정 (90 ℃ 1 M 및 60분)에서 99.9%이었다. 재래식 열공정에서와는 달리 마이크로파 공정에서 추출 합성된 수화 황산 알루미늄 시료는 빠른 결정립 성장에 의해 거대크기의 판상으로 이루어진 층상구조로 존재하였다. 마이크로파와 재래식 열공정에서 합성하여, 1100 ℃에서 하소된 시료들을 모두 구형으로 응집된 분말상의 γ-Al2O3존재하였고, 이 시료들의 비표면적은 각각 113.5와 106.6 m2/g이었고, 입자의 평균 입경은 각각 46.5와 26.3μm이었다.